How do different intraoral scanners and milling machines affect the fit and fatigue behavior of lithium disilicate and resin composite endocrowns?

The aim of this in vitro study was to evaluate the effect of the combinations of two different intraoral scanners (IOS), two milling machines, and two restorative materials on the marginal/internal fit and fatigue behavior of endocrowns produced by CAD-CAM. Eight groups (n= 10) were considered through the combination of TRIOS 3 (TR) or Primescan (PS) IOS; 4-axes (CR; CEREC MC XL) or 5-axes (PM; PrograMill PM7) milling machines; and lithium disilicate (LD; IPS e.max CAD) or resin composite (RC; Tetric CAD) restorative materials. Specific surface treatments were applied to each material, and the bonding to its corresponding Endocrown-shaped fiberglass-reinforced epoxy resin preparations was performed (Variolink Esthetic DC). Computed microtomography (µCT) was performed to assess the marginal/internal fit, as well as a mechanical fatigue test (20 Hz, initial load = 100 N/5000 cycles; step-size = 50 N/10,000 cycles until a threshold of 1500 N, then, the step-size was increased if needed to 100 N/10,000 cycles until failure or a threshold of 2800 N) to evaluate the restorations long-term behavior. Complementary analysis of the fracture features and surface topography in scanning electron microscopy was performed. Three-way ANOVA and Kaplan-Meier test (α = 0.05) were performed for marginal/internal fit, and fatigue behavior data, respectively. PS scanner, CR milling machine, and RC endocrowns resulted in a better marginal fit compared to their counterparts. Still, the PM machine resulted in a better pulpal space fit compared to the CR milling machine. Regardless of the scanner and milling machine, RC endocrowns exhibited superior fatigue behavior than LD ones. LD endocrowns presented margin chipping regardless of the milling machine used. Despite minor differences in terms of fit, the 'IOS' and 'milling machine' factors did not impair the fatigue behavior of endocrowns. Resin-composite restorations resulted in a higher survival rate compared to glass-ceramic ones, independently of the digital devices used in the workflow.

Methodological approaches in graded dental ceramics.

BACKGROUND: Functionally graded materials (FGM) with indistinct boundaries potentially eliminate the damaging stresses occurring at the interfaces. FGM applications in dental ceramics have enhanced their fatigue resistance and interfacial toughness. OBJECTIVES: This scoping review aims to map graded designs in dental ceramics, distinguish their methodological approaches with their material characteristics and properties, and understand the factors affecting the outcomes of each of the graded approaches. METHODS: A systematic electronic search was performed with the databases MEDLINE (PubMed), Scopus, Cochrane Library, EBSCO, and Google Scholar along with a manual search. RESULTS: About 2675 articles were initially found from all the searches with no date restriction till July 2023. After rejecting duplicates and based on exclusion criteria, about 52 articles were included. SIGNIFICANCE: Methodological approaches in grading such as glass-infiltration and silica-infiltration have been investigated on pre-sintered zirconia. The type of infiltration and the method of infiltrate application significantly influenced the phase transformation of zirconia, its microstructure, surface hardness, fracture toughness, flexural strength, wear, and fatigue strength of graded dental zirconia. Interlayers were accommodated between metal-ceramic and veneer-core all-ceramic layers. Fractions of zirconia-porcelain and alumina-porcelain showed high bending strength and better stress distribution. The results of finite element analysis studies predicted that using 10-layered graded layers reduced the stresses at the crown-cement-dentin interface.

The Surface Roughness of Contemporary Indirect CAD/CAM Restorative Materials That Are Glazed and Chair-Side-Finished/Polished.

The surface roughness (Ra) of indirect computer-aided design/computer-aided manufacturing (CAD/CAM)-fabricated dental restorations is crucial for their long-term durability. This study intended to evaluate the Ra of five different types of contemporary indirect CAD/CAM restorative materials with varying compositions that were glazed and finished/polished. A total of 75 specimens, disc-shaped (10 mm × 2 mm), were obtained from five materials (n = 15) (Tetric CAD, IPS e.max CAD, IPS e.max ZirCAD, CELTRA Duo, and Vita Enamic) and fabricated by CAD/CAM. One of the two surfaces for each specimen was subjected to glazing, while the other surface was subjected to finishing/polishing. The Ra of the two surfaces in micrometers (µm) was evaluated using a Profilometer, while the surface topography was examined using a scanning electron microscope. Using SPSS, the Kruskal-Wallis, post hoc Conover, and Mann-Whitney tests were used to statistically evaluate the data. A comparison of the Ra for the finished/polished surfaces of the five test materials showed significant differences (p < 0.0001). Among the finished/polished surfaces, the mean rank values of Vita Enamic were significantly higher than the other four test materials (p < 0.0001). A comparison of the Ra of glazed surfaces among the five study materials revealed significant differences (p < 0.0001). The Ra for the IPS e.max ZirCAD material was significantly higher than the rest of the four materials (p < 0.001). A comparison of the Ra for two types of surface conditioning within each of the five test materials showed a significant difference (p < 0.05). Only for IPS e.max ZirCAD was the Ra of the glazed surface significantly higher than the finished/polished surface (p < 0.0001). Significant variations in the surface roughness (Ra) were exhibited between the finished/polished and glazed surfaces of the five test materials. Hybrid ceramics showed the highest Ra values for the finished/polished surfaces, and zirconia exhibited the highest Ra values among the glazed surfaces among the tested materials. The Ra values of either finished/polished or glazed surfaces of the test materials were within the clinically acceptable range (0.2-0.5 µm), except for the glazed surface of the zirconia ceramics (0.84 µm).

A Clinician's Perspective on the Accuracy of the Shade Determination of Dental Ceramics-A Systematic Review.

BACKGROUND: No systematic review or meta-analysis has been identified that provides a clinician's perspective on the shade selection process for ceramic restorations. The aim of the present systematic review is to find and systematize the available knowledge by referring to the methods to assess the color of dental ceramics. METHODS: The final search was performed on 10 December 2023 in six search engines. The keywords used in the search strategy were as follows: ("color matching" OR "shade matching" OR "color measurement" AND "porcelain" OR "dental ceramics") AND "dentistry" AND "accuracy". RESULTS: The search strategy identified 139 potential articles. After the screening process, sixteen articles were included in the review. CONCLUSIONS: In conclusion, the most common method, the visual method, has lower accuracy and repeatability. Devices like spectrophotometers and colorimeters provide precise, repeatable, and objective measurements, but fail to be widely applied in everyday clinical practice. Clinicians should not rely solely on their senses for shade determination, but should turn to quantitative methods. Colorimetric devices connected to mobile applications are an interesting and useful tool. Software and apps based on artificial intelligence are emerging as promising tools, but they require further research.

Comparison of subcritical growth parameters of a Y-TZP obtained via cyclic or dynamic fatigue tests.

OBJECTIVE: The objective of this study was to 1) compare the stress corrosion coefficient (n) of a Y-TZP obtained by two fatigue tests: cyclic and dynamic and 2) evaluate the effect of frequency in the characteristic lifetime and the existence of interaction between the cyclic fatigue and slow crack growth. METHODS: A total of 145 Y-TZP specimens were produced in accordance with the manufacturer's instructions. These specimens, measuring 4.0 × 3.0 × 25.0 mm, were used for dynamic (n = 70) and cyclic fatigue tests (n = 75). The specimens were obtained from CAD/CAM blocks, sectioned, and sintered in a furnace at 1530 °C with a heating rate of 25 °C/min. They were tested in their "as-sintered" form without any additional surface treatment. The fatigue tests were conducted using a four-point bending to obtain the slow crack growth parameters (n). The cyclic fatigue test was also conducted in two frequencies (2 and 10 Hz), using stress levels between 350 and 600 MPa. Data from these tests were analyzed using ASTM C 1368-00 formulas and Weibull statistics. Scanning electron microscope (SEM) was used for fracture surface analysis to identify the origin of the fracture. Critical defect size was measured and used, along with flexural strength values, to estimate fracture toughness. Dynamic fatigue test data were used to obtain subcritical crack growth (SCG) parameters and perform Weibull statistical analysis. The cyclic fatigue data were used in the General Log-linear Model equation using the ALTA PRO software. Data were analyzed using one-way ANOVA followed by Tukey post-hoc tests and Student's t-test at a significance level of p ≤ 0.05. RESULTS: In the dynamic fatigue test, the values obtained for σfo and n were 667 and 54, respectively. This parameter indicates how the strength of the material diminishes over time due to internal cracks. The Weibull parameters obtained from the same test results were m = 7.9, σ0 = 968, 9 and σ5% = 767, which indicates the reliability of the material. The Weibull parameters obtained by cyclic fatigue were statistically similar for the two frequencies used, the m* was 0.17 (2 Hz) and 0.21 (10 Hz); characteristic lifetimes (η) were 1.93 × 106 and 40,768, respectively. The n values obtained by cyclic fatigue were 48 and 40 at frequencies of 2 and 10 Hz, respectively. There was no effect of the frequency, the stress level or the interaction of the two in the Y-TZP lifetime, when analysed by General Log Linear Model. SIGNIFICANCE: the n values obtained by cyclic and dynamic fatigue tests showed no statistically significant difference and the effect of frequency in the characteristic lifetime and the existence of interaction between the cyclic fatigue and subcritical growth were not observed in the tested specimens.

Additive manufacturing of dental ceramics in prosthodontics: The status quo and the future.

PURPOSE: This review aims to summarize the available technologies, material categories, and prosthodontic applications of additive manufacturing (AM) dental ceramics, evaluate the achievable accuracy and mechanical properties in comparison with current mainstream computer-aided design/computer-aided manufacturing (CAD/CAM) subtractive manufacturing (SM) methods, and discuss future prospects and directions. STUDY SELECTION: This paper is based on the latest reviews, state-of-the-art research, and existing ISO standards on AM technologies and prosthodontic applications of dental ceramics. PubMed, Web of Science, and ScienceDirect were amongst the sources searched for narrative reviews. RESULTS: Relatively few AM technologies are available and their applications are limited to crowns and fixed partial dentures. Although the accuracy and strength of AM dental ceramics are comparable to those of SM, they have the limitations of relatively inferior curved surface accuracy and low strength reliability. Furthermore, functionally graded additive manufacturing (FGAM), a potential direction for AM, enables the realization of biomimetic structures, such as natural teeth; however, specific studies are currently lacking. CONCLUSIONS: AM dental ceramics are not sufficiently developed for large-scale clinical applications. However, with additional research, it may be possible for AM to replace SM as the mainstream manufacturing technology for ceramic restorations.

Conventional-, bulk-fill- or flowable-resin composites as prosthetic core build-up: Influence on the load-bearing capacity under fatigue of bonded leucite-reinforced glass-ceramic.

This study aimed to evaluate the fatigue performance of simplified ceramic restorations (leucite-reinforced glass ceramic) adhesively cemented onto substrates of different resin composites. Three options from the same commercial line were selected (Tetric N-Line, Ivoclar), classified as Conventional (CRC), Bulk-fill (BRC) and Flowable (FRC), which were used to make discs using a cylindrical metallic device (n = 19; Ø = 10 mm, thickness = 2.0 mm). A total of 57 discs (Ø = 10 mm, thickness = 1.0 mm) were made from CAD/CAM prefabricated blocks of a leucite reinforced glass-ceramic (Empress CAD, Ivoclar) to simulate a monolithic restoration, then were randomly distributed to be bonded on 19 discs of each three different resin composite substrates (CRC; BRC; or FRC) with a dual resin cement (Multilink N; Ivoclar). The samples were subjected to a compression test with a hemispherical stainless-steel piston (Ø = 40 mm) at a monotonic regimen (n = 4; 1 mm/min loading rate and 500 kgf loading cell until fracture). The cyclic fatigue test was performed underwater at a frequency of 20 Hz (n = 15). The first step was applied using 200N for 5000 cycles, followed by increments of 50N at each step of 10,000 until failure. The outcome considered for both tests was the occurrence of radial crack. Specific statistical tests (α = 0.05) were performed for monotonic (One-way ANOVA; Tukey's test) and fatigue data (Kaplan-Meier test; Log-rank test). Fractography of fractured samples were also performed. The FRC group had the lowest failure load in both test regimes (p < 0.05; monotonic: 726.64N; fatigue: 716.67N). There were no differences between the CRC and BRC groups (p > 0.05; monotonic: 989.30 and 990.11N; fatigue: 810.00 and 833.33N, respectively). The same result was obtained considering cycles for fatigue failure (FRC < CRC=BRC). Leucite glass-ceramic bonded to substrates made of flowable resin composite behaves worse mechanically than bonding to conventional or bulk-fill resin composite substrates.

Impact of try-in paste removal on the fatigue behavior of bonded lithium disilicate ceramics.

This in vitro study assessed the effectiveness of three cleaning protocols (air-water spray, 37% phosphoric acid, or Ivoclean) on lithium disilicate restorations' fatigue behavior after try-in paste application, compared to a clean condition. Lithium disilicate discs (IPS e.max CAD, Ivoclar) with Ø-= 12 mm and 1 mm thickness were prepared from prefabricated CAD-CAM blocks, polished, subjected to CAD-CAM milling topography simulation and crystallization. After, etching with 5% hydrofluoric acid and the application of try-in paste (Variolink try-in paste shade white; load of 2.5 N for 5 min) was performed. Discs that received try-in paste were divided into three groups according to the removal protocol: SPRAY - air-water spray for 30 s; HPO - active application of 37% phosphoric acid for 60 s; IVOC - application of Ivoclean for 20 s. Control group (CTRL group) did not receive the try-in paste application. Half of the specimens (n= 15) were tested in the baseline condition (24 h up to 7 days), and the others underwent 25,000 thermal cycles (5 - 55 °C) + 210 days of distilled water storage (37 °C). Additional specimens (n= 3) underwent monotonic testing (1 mm/min). Fatigue testing involved a cyclic fatigue approach (20 Hz, initial load = 100 N - 5000 cycles, step size = 50 N - 10,000 cycles) until a visible crack appeared. Fractographic and topographic analyses were performed. Fatigue data were statistically analyzed with two-way ANOVA, Kaplan-Meier log-rank (Mantel-Cox), and independent t-test (α= 0.05). In the baseline condition, the IVOC group resulted in a superior fatigue behavior compared to the CTRL and SPRAY groups, but similar to the HPO group. The HPO and SPRAY presented a similar fatigue behavior to the CTRL group. It was noticed a decrease in fatigue behavior after aging, which resulted in all the cleaning protocols leading to similar fatigue behavior compared to the CTRL group. On the SPRAY group surface, try-in pastes remnants were noticed. In summary, despite a detrimental impact at baseline conditions, all tested cleaning protocols seem proper to remove the try-in paste from the ceramic's surface in the long-term evaluation.

Borosilicate glass as a surface finishing alternative for improving the mechanical properties of third-generation zirconia.

OBJECTIVE: This study evaluated the effect of an experimental borosilicate glass on the mechanical and optical behavior of 5Y-PSZ zirconia and comparing it to commercial glaze and as-sintered. METHODS: Disc-shaped specimens of a 5Y-PSZ (Zpex Smile) were prepared and sintered (1550 °C, 2 h). The zirconia discs were randomly divided according to the surface treatment: as-sintered (C), commercial glaze (G), and experimental borosilicate glass (SL). Glaze and experimental glass powders were mixed with building liquids and applied to zirconia with a brush. G specimens were fired at 950 °C and SL at 1200 °C. An extended dwell time of 20 min was applied to both groups. Biaxial flexural strength, roughness (Ra and Rz), translucency (TP00), color alteration (ΔE00), Vickers hardness, fracture toughness, residual stresses, and x-ray diffraction analyses were conducted. Statistical analyses were performed with Weibull statistics, Kruskal-Wallis, or ANOVA tests (α = 5%). RESULTS: SL yielded the highest flexural strength (799.35 MPa), followed by G (662.34 MPa), and C (485.38 MPa). The fracture origin of SL specimens was in the bulk zirconia, while G and C showed fractures starting at the surface. As-sintered reached the highest fracture toughness and hardness. Glaze and borosilicate glass provided surface compressive stresses. Borosilicate glass application led to phase transformation (t→m). SL and G showed the lowest roughness. TP00 and ΔE00 were similar among groups. SIGNIFICANCE: Borosilicate glass improved strength without harming the optical properties of third-generation zirconia. Toughness and roughness provided by the experimental glass were similar to those from commercial glaze.

Influences of luting cement shade on the color of various translucent monolithic zirconia and lithium disilicate ceramics for veneer restorations.

PURPOSE: The purpose of this study was to assess the effect of resin cement shade on the color of different novel ultratranslucent monolithic zirconia and lithium disilicate veneer materials. MATERIALS AND METHODS: For a total of 40 specimens, flat cylindrical discs with a 9-mm diameter and 0.5-mm thickness were created using CAD/CAM technology. The specimens were divided into five groups according to their material (n = 8) (e.max, Prettau, Aidite, Shofu and Dima) using A1 shade. Resin discs with the same diameter and shade as the specimens served as tooth-colored substructures. Three shades (neutral, light and warm) of resin cement try-in pastes (Variolink Esthetic LC) were used as the luting cement material. The color of each material group was measured before and after cementation using the three cement shades, and the CIE L*a*b* coordinates were obtained with a spectrophotometer. Values for the translucency parameter (TP) and color change delta E (E) before (baseline) and after cementation of each specimen were determined. To compare differences among the material groups within each shade of cement and among various shades of cement within each material, the data were analyzed using one-way ANOVA and post hoc testing. RESULTS: Color coordinates L*, a* and b* significantly changed after the application of try-in pastes relative to baseline values, with a noticeable decrease in lightness (L*) (P < .05). A significant color change (ΔE) was observed in all tested materials after cementation, with ΔE values exceeding 3.3 (P < .05). Although TP changed after cementation for most materials tested, these changes were not statistically significant (P > .05). Shofu and Dima ceramics showed the lowest TP values, while Aidite and Prettau showed the highest TP values. For e.max, translucency decreased after cementation with neutral and warm shades, and it significantly increased after cementation with a light shade. CONCLUSION: The shade of cement significantly altered the final color of the ceramic veneer material to a level above the threshold at which the clinical perception of color change occurred (> 3.3). The TP was not influenced by the cement shade. The translucency levels of the novel ultratranslucent multilayer monolithic zirconia ceramics Aidite and Prettau were higher than that of the lithium disilicate e.max material.

Evaluation of one versus two glaze firings on the color stability and mechanical properties of an extrinsically characterized monolithic CAD-CAM lithium disilicate glass ceramic.

PURPOSE: To evaluate the effects of 1 versus 2 glaze firings on the color and mechanical properties of an extrinsically characterized lithium disilicate ceramic after thermal cycling, brushing, or both. MATERIALS AND METHODS: Eighty specimens were divided into 2 groups: 1 glaze firing (GL1) and 2 glaze firings (GL2). Each group was subdivided into 4 groups (n = 10), according to the experimental conditions: thermal-cycling, brushing, thermal-cycling + brushing, and immersion in distilled water (control). Color variation, surface roughness, and Vickers microhardness were analyzed before each designated experiment and after the simulated periods of 2.5, 5, and 10 years. Three-way mixed ANOVA was used for all outcomes, followed by 1-way ANOVA, repeated measures 1-way ANOVA, Bonferroni post hoc test, and t-test to check for statistical differences (α = 0.05). RESULTS: Thermal cycling generated greater color changes in the GL1 group at 2.5 and 5 years (p < 0.001; p = 0.013). Brushing generated color changes in GL1 at 5 years (p = 0.003) and in GL2 at 10 years (p = 0.017). Regarding surface roughness, the GL1 group suffered alterations in thermal cycling + brushing at 5 years. In the control group, the GL1 group exhibited higher roughness values than GL2 (p < 0.05). Most of the groups experienced an increase in microhardness at 2.5 years (p < 0.05). In the GL1 group, thermal-cycling increased the microhardness at 5 years (p = 0.006); at 5 and 10 years, the GL1 group had a higher microhardness than the GL2 in thermal-cycling + brushing (p < 0.05). CONCLUSION: Ceramics with 1 glaze firing showed greater color, roughness, and microhardness changes compared to those submitted to 2 firings.

A study on the discoloration of different dental porcelain systems.

Purpose: This study aimed to investigate the discoloration of four types of dental porcelain systems (feldspathic, monolithic zirconia, lithium disilicate, and leucite glassceramic) with various surface treatments (glazed and mechanically polished) after undergoing chewing simulation against a natural tooth antagonist. Materials and methods: Disc-shaped porcelain groups (9x3mm) were produced for the following categories: feldspathic glazed (FG), feldspathic mechanically polished (FM), zirconia glazed (ZG), zirconia mechanically polished (ZM), lithium disilicate glazed (ExG), lithium disilicate mechanically polished (ExM), leucite glass-ceramic glazed (EG), and leucite glass-ceramic (EM). In vitro chewing simulation was conducted on all porcelain groups, and a spectrophotometer was used to compare the color changes between their initial states. Results: The ΔE values (discoloration) of all porcelain samples were statistically different (p <0.05), and the ΔE values of the glazed samples were higher than those of the mechanically polished samples. Conclusion: All the glazed samples are more likely to show more color change than the mechanically polished sample groups.

Effect of simulated gastric acid on aesthetical restorative CAD-CAM materials' microhardness and flexural strength.

Background: Gastric acid, which is among erosive substances, gradually rises to the mouth in individuals with reflux and bulimia nervosa disorders, and this causes various effects on dental restorations. Aim: The objective of this study is in vitro investigation of gastric acid's effect on flexural strength and hardness on aesthetic restorative computer-aided design and computer-aided manufacturing (CAD-CAM) materials. Materials and Methods: For this study, four materials have been used, namely Enamic (Vita), Superfect Zir (Aidite) Zirconia, IPS e.max CAD (Ivoclar Vivadent), and Mark II (Vita). From these four different materials, 24 samples with 14 × 4 × 1 dimensions in rectangular prism form are used, which makes a total of 96 samples. One group was separated as the control group, while the rest was allowed to wait at 37°C, 5 ml gastric acid for 96 hours. Hardness value and flexural strengths were measured as pre-exposure and post-exposure to gastric acid. Results: There is a statistically significant difference between the groups in terms of the amount of decrease in the mean hardness after exposure to gastric acid compared to pre-exposure values (p: 0,000; P < 0,05). There was no statistically significant difference between the groups in terms of the amount of decrease in the post-exposure average flexural strength compared to the pre-exposure value (p: 0.063; P > 0.05). There is a statistically significant difference between the groups in terms of the average flexural strength after exposure to the acid. Conclusions: According to the data obtained, it was concluded that exposure to gastric acid affects the hardness and flexural strength properties of dental restorative ceramic materials.

Optimized Erbium-Doped Yttrium Aluminum Garnet (Er:YAG) Laser Parameters for the Removal of Dental Ceramic Restorations.

OBJECTIVES: The use of lasers for debonding adhesively luted ceramic restorations is a rather recent oral laser application in dentistry. The removal of all-ceramic restorations in the mouth can often be a troublesome task. A novel method for the debonding of ceramic restorations without damaging the restorations is Er:YAG laser irradiation. The aim of this study was to evaluate the Er:YAG laser for debonding procedures of different dental ceramics and to identify appropriate laser settings. MATERIAL AND METHODS: Lithium disilicate, zirconium-reinforced lithium silicate, feldspatic ceramic, and zirconium dioxide were investigated. Ten ceramic rectangular-shaped specimens with 1 and 2 mm thickness were produced from each material. All specimens were irradiated with four different power settings 1.5; 2.5; 3.5; 4.5 W, pulse duration 50 µs, laser repetition rate 10 Hz, time of irradiation 10 s. The transmitted energy was measured with a powermeter. Additionally the suitability of the Er:YAG laser to remove the adhesively bonded ceramic and the time until loss of retention was evaluated. RESULTS: The transmission rate for 1 and 2 mm platelets was determined for zirconium-reinforced lithium silicate at 54.6%/35.6%, lithium disilicate at 53.2%/35.7%, zirconium dioxide at 40.6%/32.4%, and for the feldspathic ceramic at 19.4%/10.1%. For zirconium-reinforced lithium silicate and zirconium dioxide 2.5 W (250 mJ/10 Hz) was an appropriate energy level for effective debonding. Whereas for lithium disilicate and for feldspathic ceramic, 4.5 W (450 mJ/10 Hz) is required for efficient debonding. CONCLUSIONS: There are differences regarding transmission rates between ceramic types for the Er:YAG laser light and additionally depending on the type of ceramic different energy settings should be used for adequate debonding. Based on our in-vitro experiments we recommend 2.5 W for zirconium-reinforced lithium silicate and zirconium dioxide and 4.5 W for lithium disilicate and feldspatic ceramic. Transmission rates of different ceramic types and varying influences of thicknesses and bonding materials should be considered to adjust the laser parameters during laser debonding of adhesively luted all-ceramic restorations.

Evaluation of Fracture Resistance of Occlusal Veneers Made of Different Types of Materials Depending on Their Thickness.

Pathological tooth wear is an escalating social problem. Occlusal veneers can be an alternative to traditional prosthetic restorations such as crowns, inlays, and onlays. BACKGROUND: The aim of this study is to assess the fracture resistance of occlusal veneers made of various materials depending on their thickness. METHODS: In total, 120 occlusal veneers were examined. The restorations were made of four ceramics: leucite LC (IPS Empress Esthetic), hybrid HC (Vita Enamic), lithium disilicate LDC (IPS e.max Press), and zirconium oxide ZOC (Ceramill Zolid HT). A total of 30 veneers were made of each material, 10 for each of the three thicknesses: 1 mm, 1.5 mm, 2 mm. The restorations were cemented on identical abutments duplicated from the developed phantom tooth 35 (KaVo) with composite cement (All Bond Universal). The samples prepared in this way were subjected to a compressive strength test in a universal testing machine. Statistical analysis of the results was performed. RESULTS: The average fracture resistance of occlusal veneers made of zirconium oxide ceramic was 1086-1640 N, of lithium disilicate ceramics 456-1044 N, of hybrid ceramics 449-576 N, and of leucite ceramics 257-499 N. CONCLUSIONS: Occlusal veneers made of ceramics, zirconium oxide and lithium disilicate, had the highest resistance to fractures. Restorations made of leucite ceramics turned out to be the least resistant to forces. The greater the thickness of the ceramic occlusal veneers, the greater their fracture resistance.

Investigation of Spark Plasma Sintering on Microstructure-Properties of Zirconia Reinforced Fluormica Glass for Dental Restorations.

BACKGROUND: Conventional sintering methods of dental ceramics have limitations of high temperature and slow cooling rates with requirements of additional heat treatment for crystallization. Spark plasma sintering (SPS) is an emerging technique that has the potential to process dental restorations with dense microstructures and tailor-made clinically relevant properties with optimized processing parameters. This study explored the potential of the SPS of zirconia-reinforced fluormica glass (FM) for dental restorative materials. METHODS: FM glass frit was obtained through the melt-quench technique (44.5 SiO2-16.7 Al2O3-9.5 K2O-14.5 MgO-8.5 B2O3-6.3 F (wt.%)). The glass frit was ball-milled with 20 wt.% of 3 mol% yttria-stabilized zirconia (FMZ) for enhanced fracture toughness. The mixtures were SPS sintered at a pressure of 50 MPa and a heating rate of 100 °C/min for 5 min with an increase in temperature from 650-750 °C-850 °C-950 °C. Phase analysis was carried out using XRD and microstructural characterization with SEM. Micro-hardness, nano-indentation, porosity, density, indentation fracture toughness, and genotoxicity were assessed. CONCLUSIONS: The increase in the SPS temperature of FMZ influenced its microstructure and resulted in reduced porosity, improved density, and optimal mechanical properties with the absence of genotoxicity on human gingival fibroblast cells.

Interface adhesion on layered zirconia: Effects of the veneering ceramic material and veneering technique.

PURPOSE: To evaluate the effect of different veneering ceramics and veneering techniques on the bond strength to zirconia. MATERIALS AND METHODS: 3Y-TZP zirconia blocks were sliced into 60 slabs, polished, and sintered. Each slab received one ceramic cylinder (Ø = 3.4 mm, 5 mm-high), according to the veneering ceramic type (feldspathic-FEL or lithium disilicate-based-LD) and the veneering technique (file-splitting with resin-based luting agent-RC, file-splitting with fusion ceramic-FC, or heat-pressing-HT), which resulted in six groups: FEL-RC, FEL-FC, FEL-HT, LD-RC, LD-FC, LD-HT. After preparation, the samples were immersed in distilled water for 24 h before the shear bond strength (SBS) test. The failure modes were classified as adhesive, predominantly adhesive, or cohesive. Representative failure mode images were taken in a Scanning Electron Microscope. The SBS data were analyzed by two-way ANOVA and Tukey's test. RESULTS: Both type of veneering ceramic and technique affected the bond strength. FC led to the highest SBS values. RC and HP provided similar results when compared within each veneering ceramic. Lithium disilicate achieved lower bond strength than feldspathic ceramic when the heat-pressing technique was applied. The most frequent failure modes were predominantly adhesive and adhesive for FEL and LD, respectively. CONCLUSION: File-splitting with fusion ceramic provided the highest adhesion to zirconia when feldspathic or lithium disilicate-based ceramics were used. The heat-pressing technique for veneering with lithium disilicate significantly decreased the bond strength when compared to the feldspathic ceramic.

Preheated Composite as an Alternative for Bonding Feldspathic and Hybrid Ceramics: A Microshear Bond Strength Study.

PURPOSE: To evaluate the bond strength between alternative or conventional luting agents and indirect restorative materials. MATERIALS AND METHODS: Blocks of a polymer-infiltrated ceramic network (PICN, Vita Enamic) and a feldspathic ceramic (FEL, Vita Mark II) were sliced and divided according to the luting agent: resin cement (PICN-RC, FEL-RC), flowable composite (PICN-FC, FEL-FC), or preheated composite (PICN-PH, FEL-PH). The ceramic surfaces were polished, etched with 5% hydrofluoric acid for 60 s, and then a silane layer was applied. Cylinders of the luting agents were built up on the ceramic surfaces. In half the samples, the microshear bond strength (µSBS) was tested after 24 h (baseline). The other half was tested after 5000 thermocycles (5°C-55°C) (aging). The failure modes were determined using a stereomicroscope, and the ceramic surfaces were analyzed using a scanning electron microscope. Data were statistically analyzed with two-way ANOVA. RESULTS: Thermocycling reduced the bond strength values of all experimental groups. Regarding FEL, the preheated composite obtained the highest results. Resin cement showed results similar to the flowable composite at baseline and after aging. The highest results of PICN were obtained from the preheated composite followed by resin cement and flowable composite. Significant differences among the three luting agents were observed before and after aging. The most frequent failures among the experimental groups were adhesive and cohesive in the ceramic. CONCLUSION: Bond strength results indicate that the preheated composite can be an alternative for adhesive cementation when applied on the tested feldspathic ceramic or PICN.

Evaluation of the marginal fit of lithium disilicate single crowns fabricated with the conventional (Emax press) and the CAD/CAM (Emax CAD) method: A systematic review and meta-analysis.

AIM: The purpose of this systematic review and meta-analysis is to evaluate the marginal adaptation of single unit full coverage lithium disilicate fixed dental restorations fabricated with the conventional heat pressed technique and the digital CAD/CAM workflow. MATERIALS AND METHODS: This study is according to the Preferred Reporting Items for Systematic Reviews and Meta- Analyses (PRISMA) statement. study research was conducted in MEDLINE via PubMed and Cochrane Library databases together with a hand search of studies published until June 2022. The search terms were combining suitable Medical Subject Headings (MeSH terms) together with free text words in single or multiple conjunctions. A modified methodological index was used to assess the risk of bias of the included studies. A random effect model was applied to pool the effect estimates, and further assessment of the heterogeneity across studies using the Q test and the I2 metric was conducted. All statistical analyses were performed using Rstudio software, version 4.1.2, using the "meta" package. RESULTS: The electronic search and hand search identified 51 articles. Eighteen met the inclusion criteria and were included in the systematic review, 17 of which were in vitro and only one was an in vivo study. However, 17 of the initial 18 could be included in the meta-analysis, due to lack of statistical data in one of the in vitro studies. Statistical analyses were conducted by using the Rstudio software program. Meta-analysis was performed with the random effects model (α=.05). No statistical difference was found between the two fabrication methods (p-value=0.49). CONCLUSIONS: Although the mean marginal adaptation of lithium disilicate single crowns was found to be better with the heat-pressed technique, there was no statistical significance with the CAD/CAM fabricated restorations and both resulted in a clinically acceptable result. Nonetheless, more clinical studies are needed for safer conclusions.

Ceramic versus Composite Resin Polishing Systems on the Surface Roughness of Milled Leucite-Reinforced Ceramics.

Background and Objective: This study aimed to compare the surface finish of milled leucite-reinforced ceramics polished with ceramic and composite polishing systems based on the manufacturers' recommendations. Materials and Methods: Sixty subtractive computer-aided manufactured (s-CAM) leucite-reinforced glass-ceramic specimens (IPS-Empress-CAD) were assigned into six groups: no polishing, a ceramic polishing kit, and four composite kit groups. The roughness average (Ra) was evaluated in microns using a profilometer, and scanning electron micrographs were obtained for qualitative analysis. A Tukey HSD posthoc test (α = 0.05) was used to determine significant intergroup differences. Results: After surface evaluation of the ceramics, the Ra values of the polishing systems ranked OptraFine (0.41 ± 0.26) < Enhance (1.60 ± 0.54) < Shofu (2.14 ± 0.44) < Astropol (4.05 ± 0.72) < DiaComp (5.66 ± 0.62) < No Polishing (5.66 ± 0.74). Discussion: Composite polishing systems did not provide as smooth surfaces as the ceramic polishing kit for CAD-CAM leucite-reinforced ceramics. Thus, using ceramic polishing systems, polishing leucite ceramics is recommended, whereas composite polishing systems should not be considered as an alternative for use in minimally invasive dentistry.